An in-service failure of a thin-walled titanium bleed-air duct from a wide-bodied commercial aircraft has been investigated. Cracking had occurred in the heat-affected zone (HAZ) adjacent to a circumferential weld joining two sections of the duct which was manufactured from commercially pure (grade 3) titanium sheet. Specimens were cut from the duct to include an intact weld and tested under known conditions (overload, fatigue, sustained loading) for comparison with the failed duct. Metallographic observations showed that cracking occurred through an acicular alpha HAZ, and fractographic observations revealed brittle, cleavage-like cracking with occasional areas of fatigue striations for both the failed duct and fatigued specimens. These observations, and the absence of sustained-load cracking in test specimens, suggested that the in-service failure had occurred primarily by fatigue. Observations also indicated that small, cleavage-like cracks had been present in the ducts prior to service, although whether these cracks were caused by overload tearing, stress-corrosion cracking, hot-salt cracking or fatigue was not clear. Other possible causes of cleavage-like cracking, e.g. the presence of hydrides as proposed for previous failures, contamination of HAZs by oxygen/nitrogen, are discussed. Possible ways of preventing further failures are then outlined.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failures of welded titanium aircraft ducts


    Weitere Titelangaben:

    Versagen von geschweißten Titanrohrleitungen an Flugzeugen


    Beteiligte:
    Lynch, S.P. (Autor:in) / Hole, B. (Autor:in) / Pasang, T. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1995


    Format / Umfang :

    17 Seiten, 15 Bilder, 30 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Failures in welded ships

    Engineering Index Backfile | 1952


    Research on welded bridge failures

    Engineering Index Backfile | 1941


    Damage Evolution in Thin-Walled Titanium Ducts for use in Aircraft Pneumatic Systems

    Adib, Anthony M. L. / Baptista, Carlos A. R. P. / Andrade, Margareth et al. | SAE Technical Papers | 2007


    Instrument Panel Structure Utilizing Linear Welded A/C Ducts

    Van Kirk, L. J. / Waterloo, R. L. | SAE Technical Papers | 1987