The corrosion behavior of coated materials after painting were investigated in cyclic corrosion tests and outdoor exposing tests. The coatings of pure Zn, Zn-Fe alloy, Zn-Ni alloy, and Zn-Co-Cr alloy with dispersed particles of Al2O3 were submitted to the tests. Several cyclic corrosion tests whose time ratio of wet environments in a cycle were different from each other were conducted. The outdoor exposing tests were also carried out at the seashores in both Okinawa and Chiba, Japan. The samples were sprayed with seawater twice a week in the test at Chiba to accelerate corrosion. Corrosion properties of samples were estimated by the blistering width at the knife-cut. In a cyclic corrosion test which contains less than 40 % of wet environment in a cycle the coated materials were proved to have an excellent anti-blistering property comparing with cold rolled steel sheet. The results of the two outdoor exposing test proved that the coated materials more than 30 g/m2 of Zn and Zn-alloy have satisfactory anti corrosion property after painting but that the decrease in coating weight to 20 g/m2 makes the property unstable independantly of the kind of coating. Among the tested materials, the Zn-Co-Cr alloy containing dispersed particles of Al2O3 showed the highest resistance for blistering.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Cosmetic corrosion of Zn alloy coated sheet steels


    Weitere Titelangaben:

    Kosmetische Korrosion von mit Zinklegierung beschichteten Stahlblechen


    Beteiligte:
    Yasuda, A. (Autor:in) / Umino, S. (Autor:in) / Kyono, K. (Autor:in) / Yamato, K. (Autor:in)


    Erscheinungsdatum :

    1988


    Format / Umfang :

    7 Seiten, 9 Bilder, 4 Tabellen, 10 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    An Evaluation of Cosmetic Corrosion Performance of Zinc and Zinc Alloy Coated Steels

    Gray, B. M. / Davidson, D. D. / Stephens, M. L. et al. | SAE Technical Papers | 1986


    An Evaluation of Cosmetic Corrosion Performance of Zink and Zink Alloy Coated Steels

    Gray,B.M. / Shaffer,R.J. / Stephens,M.L. et al. | Kraftfahrwesen | 1986


    Cosmetic Corrosion Mechanism of Zinc and Zinc Alloy Coated Steel Sheet for Automobiles

    Nishimura, Kazumi / Kitayama, Minoru / Naito, Shigeru et al. | SAE Technical Papers | 1985


    Cosmetic corrosion mechanism of zinc and zinc alloy coated steel sheet for automobiles

    Miyoshi,Y. / Kitayama,M. / Nishimura,K. et al. | Kraftfahrwesen | 1985


    Corrosion behavior of painted zink and zink alloy coated autobody sheet steels

    Roberts,T.R. / Robbins,D.J. / Smith,D.M. et al. | Kraftfahrwesen | 1986