This paper describes the oxidation of Si (001) surfaces at room temperature in a hyperthermal atomic oxygen beam. The laser-detonation-type atomic oxygen beam source, originally designed by Physical Sciences Inc., was used in this study. An intense 5 eV atomic oxygen beam with a fluence of 1019 atoms/cm2 oxidized Si surfaces to a depth of 4.5 nm. X-ray photoelectron spectra and Fourier transform infrared spectra indicate that the amount of suboxide is large and intrinsic stress is incorporated at the silicon/oxide interface. This intrinsic stress restricts the diffusivity of atomic oxygen in the oxide film. These results suggest that a silicon dioxide overlayer for protecting materials from atomic oxygen degradation in low Earth orbit must be at least 4.5 nm thick. However, a 3.5-nm-thick film protected the underlying substrate on samples flown on the EOIM-3 flight experiment. This discrepancy can be explained by the emission of Si atoms at the Si/SiO2 interface to the SiO2 film under the extremely high compressive stresses.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Oxidation of room temperature silicon (001) surfaces in a hyperthermal atomic oxygen beam


    Beteiligte:
    Tagawa, M. (Autor:in) / Ema, T. (Autor:in) / Kinoshita, H. (Autor:in) / Umeno, M. (Autor:in) / Ohmae, N. (Autor:in) / Minton, T.K. (Autor:in)


    Erscheinungsdatum :

    1997


    Format / Umfang :

    5 Seiten, 2 Bilder, 3 Tabellen, 25 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Hyperthermal-Atomic-Oxygen Generator

    Outlaw, R. A. | NTRS | 1993


    Generating Hyperthermal Atomic Oxygen

    Outlaw, Ronald A. | NTRS | 1988


    DSMC Simulations of Hyperthermal Oxygen Beam Exposures

    Cline, Jason / Minton, Timothy / Braunstein, Matthew | AIAA | 2004