Cold spraying is increasingly being used for reconstruction or repair of damaged aluminium alloy components, especially in the aviation industry. Both thin (<0.5 mm) and thick (up to 1 cm) coatings are necessary to achieve dimensional recovery of such components. Thin and above all thick coatings can be deposited in a single pass (single layer) or in several passes (multi-pass), resulting in different thermal and stress effects in the component and the coating itself. The thermal input, the amount and type of residual stresses and the porosity affect various characteristics such as adhesion, crack propagation and mechanical properties of the coating. In this study, two sets (single- and multi-pass) of aluminium alloy (AA6061) coatings with different thicknesses (0.5 mm to 2 mm) were deposited onto AA6061 substrates and compared using metallographic and fractographic analyses, four-point bending testing, residual stress analysis and Vickers microhardness indentation. Finally, the coating adhesion and cohesion were measured using the standard ASTM-C633 adhesion test and tubular coating tensile test. This study demonstrates that the single-layer strategy results in greater adhesion and lower porosity, while multilayer coatings have higher elastic modulus. Independent of the strategy, the compressive residual stress decreases as a function of coating thickness.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Different Cold Spray Deposition Strategies: Single- and Multi-layers to Repair Aluminium Alloy Components


    Beteiligte:
    Rech, Silvano (Autor:in) / Trentin, Andrea (Autor:in) / Vezzu, Simone (Autor:in) / Vedelago, Enrico (Autor:in) / Legoux, Jean-Gabriel (Autor:in) / Irissou, Eric (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2014


    Format / Umfang :

    14 Seiten




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Spray formed aluminium alloy components for automotive applications

    Sano, H. / Tokizane, N. / Ohkubo, Y. et al. | Tema Archiv | 1993


    Methods for cold spray repair

    WIDENER CHRISTIAN / WELL ADAM / BRITTON OWEN et al. | Europäisches Patentamt | 2018

    Freier Zugriff

    Repair welding of aluminium alloy wheels

    Gregory, J.T. / Kirby, B.M. | Tema Archiv | 1996


    Cast aluminium alloy automotive components

    Campbell,J. / Triplex-Zeus,GB | Kraftfahrwesen | 1989


    MASKING PLUG FOR COLD SPRAY REPAIR AT COUNTERBORE HOLE

    LE DO YOUNG HANH | Europäisches Patentamt | 2017

    Freier Zugriff