Stroncoat belongs to a new family of zinc magnesium coatings developed in Europe with comparable phase composition and properties. Their range in composition goes from 1wt% for Mg and Al, respectively, to 3wt% Mg and 3,7wt% Al, the remainder being zinc, whereas Stroncoat as a typical member contains 1,6wt% Mg and Al, respectively. All of these coatings have been proven to yield high corrosion protection, especially under salt rich lab test conditions. This has put the question, whether the possible advantages can be saved throughout the process chain of building the body-in-white. Several key aspects of forming and joining properties of Stroncoat were benchmarked with established zinc coatings in state-of-the-art lab tests. Particular interest was put on resistance spot weldability, adhesive joint strength in aged and unaged condition as well as on zinc abrasion and galling during deep drawing. Stroncoat was found to be compatible with standard processes, bringing additional benefit to car manufacturing. Many properties can be characterized in the lab, while some may only be understood during a production trial. Very often there is a relevant interdependency between the coated sheet steel and the individual manufacturing process.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Performance of a ZM-coating with 1.6% Mg and 1.6% Al in the autobody process chain


    Weitere Titelangaben:

    Performance einer ZM-Beschichtung mit 1.6% Mg und 1.6% Al in der Prozesskette zur Herstellung von Karosserien


    Beteiligte:
    Koll, T. (Autor:in) / Beier, F. (Autor:in) / Böddeker, T. (Autor:in) / Hinkel, M. (Autor:in) / Fritzsche, C. (Autor:in) / Schulz, S. (Autor:in)


    Erscheinungsdatum :

    2014


    Format / Umfang :

    8 Seiten, 8 Bilder, 7 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Variation in autobody adhesive curing process

    Wu,X. / Hao,H. / Zhang,G. et al. | Kraftfahrwesen | 1999


    Variation in Autobody Adhesive Curing Process

    Renault, Cindy / Frendberg, Dale / Zhang, Guohua et al. | SAE Technical Papers | 1999


    Technoeconomic evaluation of autobody materials

    George, S.C.H. / Evans, M. / Lowe, K. | Tema Archiv | 1997


    Autobody stamping technology progress : papers

    Society of Automotive Engineers / Ferrous Committee | TIBKAT | 1991


    Dynamic denting of autobody panels

    Burley,C.E. / Niemeier,B.A. / Koch,G.P. et al. | Kraftfahrwesen | 1976