Corrosion behaviours of low alloy steels with various alloying element contents were studied in simulated corrosion environment (pH=0.85, 10% NaCl solution) of cargo oil tank (COT) bottom plate corrosion environment. Corrosion rate was measured, and the surface morphology of test steels was characterised using scanning electron microscope (SEM). The electrochemical results were investigated using polarisation curves and electrochemical impedance spectroscopy (EIS). The corrosion behaviour of inclusion was investigated using in situ SEM images and energy disperse spectroscopy (EDS) analysis. The effect of misorientation distribution on corrosion resistance of steel was evaluated using electron backscattered diffraction microscopy. The results showed that MnS dissolved into the simulated COT corrosion solution before steel matrix, whereas TiO2 would not be dissolved. A 10-20 µm area was formed as a circular cathode around inclusion centre. The corrosion was inclined to occur in the place where curvature radius of inclusion is small. An increase in the proportion of low energy grain boundaries was conducive to the improvement of corrosion resistance especially in the early stages of corrosion.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Influence of inclusion and grain boundary on corrosion behaviour of low alloy steel in cargo oil tank bottom plate environment


    Weitere Titelangaben:

    Einfluss von Einschlüssen und Korngrenzen auf das Korrosionsverhalten von niedriglegiertem Stahl als Bodenplatte eines Öltransportbehälters


    Beteiligte:
    Liang, J.M. (Autor:in) / Wu, H.B. (Autor:in) / Tang, D. (Autor:in) / Zhang, P.C. (Autor:in) / Liu, X.T. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2014


    Format / Umfang :

    10 Seiten, 12 Bilder, 4 Tabellen, 24 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Corrosion resistant steels for inner bottom plates of cargo oil tank

    Inohara, Yasuto / Nishimura, Kimihiro / Nakamura, Masayoshi | Tema Archiv | 2007


    Cargo bottom supporting plate for V-shaped storage bin cargo ship

    ZHAO MINGYUE | Europäisches Patentamt | 2020

    Freier Zugriff

    Turtle-type trolley for lightering stainless steel segments at inner bottom in liquid cargo tank

    DAI WEI / DENG QINGBIAO / YANG ZEWEI et al. | Europäisches Patentamt | 2024

    Freier Zugriff

    Cargo tank

    HAN SANG MIN | Europäisches Patentamt | 2019

    Freier Zugriff

    Cargo tank

    KWAK KI KON / YUN KYUNG TAE / KIM BUM WOOK et al. | Europäisches Patentamt | 2018

    Freier Zugriff