Two-pass two-sided welding is widely applied to manufacture large-diameter pipes for main gas and oil pipelines. It is obvious that metal of the welds that are the first to make is subjected to repeated heating in making the subsequent pass. The study is dedicated to evaluation of the effect of repeated heating on properties of the weld metal of the two-sided welded joints on pipes made from increased-strength microalloyed steels. Investigations were carried out on the weld metal of welded joints on the pipes made from ferritic-pearlitic steels of strength category K56-K60 and of different microalloying types (10(09)G2FB, 10G2FT, 10G2T, etc.). Impact toughness, hardness and peculiarities of structural characteristics of the inside weld metal of the welded joints on pipes subjected to repeated heating in making the outside weld were evaluated. It was shown that decrease in impact toughness of test specimens of the two-pass two-sided welded joints on the pipes, the tested section of which comprises the metal of intersection of the inside and outside welds, is caused by the presence of the local embrittlement zones forming in the inside weld metal due to its heating in making the outside weld. Investigations, including by transmission electron microscopy combined with microdiffraction, detected the following two zones present in the inside weld metal: low-temperature zone (heating to 450-650 °C) caused by occurrence of the dispersion hardening processes, and high-temperature zone (heating to 950-1100 °C) related to the MAC-phase containing a substantial amount of a more stressed lath martensite and forming as a result of decomposition of non-homogenised austenite.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Properties of the weld metal of two-sided welded joints on pipes made from increased-strength microalloyed steels


    Beteiligte:
    Rybakov, A.A. (Autor:in) / Semyonov, S.E. (Autor:in) / Filipchuk, T.N. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2013


    Format / Umfang :

    6 Seiten, 6 Bilder, 3 Tabellen, 8 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Microalloyed high-strength steels

    Olsson, Kennet / Gladh, Magnus / Hedi, Jan-Erik et al. | Tema Archiv | 2006


    Strength of welded aircraft joints

    Brueggeman, W.C. | Engineering Index Backfile | 1937


    The fatigue properties of spot welded, adhesive bonded and wildbonded joints in high strength steels

    Jones,T.B. / Williams,N.T. / British Steel Corp.,GB | Kraftfahrwesen | 1986