The quality of the working rollers from ductile-cast-iron used for rolling rails is determined by the chemical and structural composition of the material of the rollers and the production technology. The requirements of the quality cannot be ensured without perfect knowledge of the course of solidification, cooling and heat treatment of the cast rollers as well as the kinetics of the temperature field of the casting and mould. An original application of ANSYS simulated the forming of the temperature field of the entire system. In the experimental investigation of temperature field, an original methodology for the measurement of the distribution of temperatures and heat flows in the roller-mould system had been developed and verified in the operation. The kinetics of the solidification has a measurable and non-negligible influence on the chemical and structural heterogeneity of the investigated type of ductile-cast-iron. Tying on to the results of the model of the temperature field of the cast rollers, an original methodology was developed for the measurement of chemical microheterogeneity. The structure of this cast-iron is created by a great amount of the transition form of graphite and small amount of globular graphite and also lamellar graphite and cementite, whereas the structure of the metal matrix is perlitic. The chemical and structural heterogeneity of the cast roller is therefore a significant function of the method of melting, modification and inoculation and the successive procedures of risering, casting and crystallization after cooling.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    The temperature field of a gravitationally cast ductile-cast-iron roller and its chemical and structural heterogeneity


    Beteiligte:
    Kavicka, F. (Autor:in) / Dobrovska, Jl (Autor:in) / Stransky, K. (Autor:in) / Sekanina, B. (Autor:in) / Stetina, J. (Autor:in)


    Erscheinungsdatum :

    2013


    Format / Umfang :

    12 Seiten, 7 Bilder, 4 Tabellen, 6 Quellen





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    ALLOY CAST IRON FOR VEHICLE SUSPENSION COMPONENT AND THE AUSTEMPERED DUCTILE CAST IRON COMPONENT

    LEE SANG DEOK / SONG SOO YOUNG / KIM JONG SOO et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Application of induction hardening ductile cast iron gears

    Morita,A. / Takagi,S. / Kawasaki,M. et al. | Kraftfahrwesen | 1984


    Application of induction hardening ductile cast iron gears

    Morita, A. / Takagi, S. / Kawasaki, M. | Tema Archiv | 1984


    A Ductile Cast Iron Material For Engine Components

    Reimann,F. / Buderus,Wetzlar | Kraftfahrwesen | 1978


    Cast iron - a ductile material for high loaded components

    Wilhelm,L. / George Fischer,CH | Kraftfahrwesen | 1987