The effects of service environment will cause corrosion damage and fatigue cracks to initiate and grow, compromising structural integrity of the aircraft aluminum alloy structure. To develop an effective inspection and maintenance-scheduling program that takes advantage of life extension technologies, the sustainment engineering and residual life prediction method of aging aircraft aluminum alloy structure at service environment was proposed in this article. The whole algorithm of the sustainment engineering was described and the included situations of repairs, corrosion damage and widespread fatigue damage on aircraft structures were presented. At last, combining the results of FEM calculation with the AFGROW software of crack growth analyses, the residual life of corroded aluminum alloy structure was estimated.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Sustainment Engineering and Residual Life Prediction of Aluminum Alloy Structure at Service Environment


    Beteiligte:
    Zhang, Qian (Autor:in) / Liu, Gang (Autor:in) / Wu, Cun-Li (Autor:in)


    Erscheinungsdatum :

    2013


    Format / Umfang :

    4 Seiten




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    A Life Cycle Systems Engineering Approach to Sustainment

    Canner, M. / IEEE / AIAA | British Library Conference Proceedings | 2003


    Simulator Sustainment Mgt

    B. L. Bell | NTIS | 2010



    Aircraft sustainment and repair

    Jones, Rhys ;Baker, Alan ;Matthews, Neil | SLUB | 2018