The premature failure of pipeline expander segments made of AISI D2 tool steel has been studied. After collecting the historical data of the segments, three possibilities were taken into account regarding the failures. Namely, the undesirable electrical discharge machining (EDM) performed on the segments, environmentally assisted cracking (EAC), and fatigue. Analysis of the cleaning water used in the pipe milling process was also performed which indicated high concentrations of sulphate and chloride ions which invigorated this assumption that corrosion played a role in the failure. However, relatively good corrosion resistance of the alloy and microscopic observations hinted to the more decisive role of the sharp cracks formed due to poor EDM on the sides of the failed segments. These cracks were held responsible for the premature failure of the segments.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Failure of pipeline expander segments due to undesirable EDM


    Beteiligte:
    Oskuie, A.A. (Autor:in) / Shahrabi, T. (Autor:in) / Lajevardi, A. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2013


    Format / Umfang :

    13 Seiten, 21 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Installing pipeline segments within a conduit

    MOUSAVI SEYD HOSSEIN / SOLEIMANI MOHAMAD ALI / SOHBATLOO ASHKAN et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    INSTALLING PIPELINE SEGMENTS WITHIN A CONDUIT

    MOUSAVI SEYD HOSSEIN / SOLEIMANI MOHAMAD ALI / SOHBATLOO ASHKAN et al. | Europäisches Patentamt | 2021

    Freier Zugriff

    GROMMET EXPANDER

    KIM JUNG HO | Europäisches Patentamt | 2018

    Freier Zugriff

    Study investigates damage to cased pipeline segments

    Song, Fengmei / Bichon, Barron / Fassett, Robert et al. | Tema Archiv | 2009


    Bicycle expander

    MA YUN | Europäisches Patentamt | 2015

    Freier Zugriff