Crack tip opening displacement (CTOD) tests were carried out on different positions of X70, X80 and X100 pipe by three-point bend testing method. The results show that the crack propagation resistance and the tear modulus of base metal, heat affected zone (HAZ), and weld of X70 and X80 pipe are larger than that of X100 pipe. At the same time, The initial CTOD values and the CTOD values withmaximum load of X70 and X80 pipe are larger than that of X100 pipe. The test results suggest that the fracture toughness, crack initiation and propagation resistance of theX70 and X80 pipe are greater than that of X100 pipe, and the mechanismis analyzed finally.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Experimental Research on Fracture Toughness of High Grade Line Pipe


    Beteiligte:
    Xiong, Qing-Ren (Autor:in) / Zhang, Jian-Xun (Autor:in) / Feng, Yao-rong (Autor:in) / Wang, Hai-tao (Autor:in) / Ma, Qiu-Rong (Autor:in) / Xu, Zhen-Zhen (Autor:in)


    Erscheinungsdatum :

    2012


    Format / Umfang :

    4 Seiten




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Fracture toughness of grade D ship steel

    Sumpter, J.D.G. / Kent, J.S. | Tema Archiv | 2006


    Dynamic fracture toughness at crack initiation, propagation and arrest for two pipe-line steels

    Pluvinage, G. / Krasowsky, A.J. / Krassiko, V.W. | Tema Archiv | 1992


    Development of API X-80 grade electric resistance welding line pipe with excellent low temperature toughness

    Nakata, Hiroshi / Kami, Chikara / Shiotani, Osamu et al. | Tema Archiv | 2005


    Development of high toughness X70 grade clad steel pipe for natural gas transportation pipelines

    Kayano, Rinzo / Nitta, Yukio / Sato, Shinya et al. | Tema Archiv | 2007


    Fracture toughness testing

    Srawley, John E. / Brown, William F. | TIBKAT | 1965