The near-threshold fatigue crack growth behavior and crack closure of three pipeline steels, - X65, X70 and X80 steels, - were investigated in air at a load ratio R of 0.1. With increase in the grade of pipeline steel, the average grain size of ferrite decreased and yield and tensile strength increased. In the near-threshold regime, the X80 steel had the slowest fatigue crack growth rate while the X65 steel had the fastest fatigue crack growth rate. The fatigue crack growth rate of the X70 steel was in-between those of the X65 and X80 steels in the near-threshold regime. For the X65 and X70 steels, it had been shown that the crack closure levels (Kcl/Kmax) were 0.1 and independent of stress intensity factor range ΔK. In contrast, the crack closure level of the X80 steel was 0.54 at the fatigue threshold and decreased with increasing ΔK. From analysis of fracture surface roughness, it was found that the factors characterizing roughness-induced crack closure for three pipeline steels in air were average fracture surface roughness, Ra, and the effective range of the crack tip opening displacement, (ΔCTOD)eff. It is concluded that the crack closure phenomenon of the X80 steel in the low delta K region is roughness-induced.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Near-threshold fatigue crack growth behavior and crack closure of natural gas pipeline steels


    Weitere Titelangaben:

    Schwellwertnahes Verhalten der Ermüdungsrissausbreitung und Rissschließung von Rohrstählen für Erdgaspipelines


    Beteiligte:
    Kim, Young-Pyo (Autor:in) / Kim, Cheol-man (Autor:in) / Kim, Woo-sik (Autor:in) / Song, Kyo-soo (Autor:in) / Shin, Kwang-Seon (Autor:in)


    Erscheinungsdatum :

    2011


    Format / Umfang :

    8 Seiten, 8 Bilder, 3 Tabellen, 16 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Near threshold fatigue crack growth in structural steels

    Rudd, W.J. / Booth, G.S. | Tema Archiv | 1998


    Assessment of pipeline fatigue crack-growth life

    Jaske, Carl E. | Tema Archiv | 2007


    Fatigue Crack Closure and Fatigue Thresholds

    Le May, I. / International Committee on Aeronautical Fatigue | British Library Conference Proceedings | 1997


    Fatigue Crack Propagation Behavior in Railway Steels

    Peixoto, D.F.C. / Ferreira, L.A.A. / de Castro, P.M.S.T. et al. | British Library Conference Proceedings | 2012