Full-scale rupture tests were conducted on 508 mm (20 in) diameter API X-60 5,7 mm wall thickness pipes containing either axial semi-elliptical cracks or simulated corrosion defects with equivalent depths ranging from 20 to 60 percent of thickness. In the case of the cracks, the failure pressures were predicted with reasonable accuracy when considering a level 3 failure assessment diagram (FAD) procedure based on API 579, as compared to level 2 FAD, since the mechanical properties were known. In both cases, the accuracy improved for shallower cracks. Considering simulated corrosion defects, the RSTRENG approach provided more reliable results on predicting the collapse pressure. For a similar depth and profile, the cracked pipes failed at a lower pressure than those containing simulated corrosion defects of equivalent depth.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Evaluation of crack and simulated corrosion defects in an API X-60 gas pipeline steel


    Weitere Titelangaben:

    Untersuchung der Schädigungen durch Risse und simulierte Korrosionswirkung in einem Stahl der Festigkeitsklasse API X-60 für Rohre der Erdgasfernleitungen


    Beteiligte:
    Hosseini, A. (Autor:in) / Cronin, D. (Autor:in) / Plumtree, A. (Autor:in)


    Erscheinungsdatum :

    2010


    Format / Umfang :

    11 Seiten, 5 Bilder, 4 Tabellen, 10 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Susceptibility of welded X80 pipeline steel to corrosion in simulated soil solution

    Ren, C.Q. / Xian, N. / Wang, X. et al. | Tema Archiv | 2012


    Study of AC corrosion on coated pipeline steel in simulated soil solution

    Xu, Xin / Xu, Lining / Liu, Wei et al. | Tema Archiv | 2011


    Transgranular stress corrosion cracking of X-60 pipeline steel in simulated ground water

    Zhang, X.Y. / Lambert, S.B. / Sutherby, R. et al. | Tema Archiv | 1999


    Seismic Performance Analysis of Oil Pipeline with Crack Defects

    Wang, Li-Li / Zhang, Xiao-Qing / Xu, Liang-Liang | Tema Archiv | 2013


    Effect of corrosion medium composition on rate of crack growth in X70 pipeline steel

    Arabey, A.B. / Bogdanov, R.I. / Ignatenko, V.E. et al. | Tema Archiv | 2011