This paper presents the findings of a weldability study of drawn arc stud welding various advanced high strength steels (AHHS) including Usibor, uncoated Boron steel and HC500C (DP800) of various thicknesses and coatings from several automakers and benchmarked against mild steel. M6 wide top (or large flange) stud is used in the study. Instead of poking for a 9-box weld lobe from trial-and-error, a robot is used to comb a 3D weld parameter space of arc current, arc time and lift height, with a parameter grid of 380 to 1.200 welds for each AHHS grade. A Design of Experiments (DOE) approach maps out the relationship between DOE inputs of control variables and DOE outputs of weld quality statistically. The objective and subjective weld quality are measured, including destructive conical bend for weld strength, dimple, sag, burn-through, head melting, cracking, excessive expulsion and backside marking. Among the 3,496 welds visually classified, photographed from both sides and destructively tested, it is found that not all AHHS behave the same in drawn arc welding. AHHS of different type, thickness and coating exhibits different welding characteristics. Mild steel as a baseline has the classic C or kidney shaped operating lobe and the best weldability characterised by the largest lobe size and tolerance to lift. Uncoated Boron steel of 1.2 mm and 1.4 mm thickness has excellent weldability at lower lift, with deteriorating performance at higher lift. It is best welded at hot and fast settings. Usibor of 1.4 mm thickness has marginal weldability. It is best welded at slow and cool settings. At 1.0 mm thickness it cannot pull 70% nugget at optimum settings. HC500C of 0.8 mm thickness has unacceptable weldability but shows potential in very hot and fast settings.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Weldability of advanced high strength steel drawn arc stud welding


    Beteiligte:

    Erschienen in:

    Welding and Cutting ; 10 , 1 ; 36-47


    Erscheinungsdatum :

    2011


    Format / Umfang :

    12 Seiten, 22 Bilder, 5 Tabellen, 9 Quellen


    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Weldability of high strength steels in wet welding conditions

    Fydrych, Dariusz / Łabanowski, Jerzy / Rogalski, Grzegorz | Online Contents | 2013


    WELDABILITY, WELDING METALLURGY, WELDING CHEMISTRY

    Sarjito Jokosisworo | DOAJ | 2012

    Freier Zugriff

    Tailored blanks of high strength steel sheets - Weldability and formability

    Uchihara, M. / Hirose, Y. / Fukui, K. | Tema Archiv | 1998


    Tailored Blanks of High Strength Steel Sheets - Weldability and Formability

    Uchihara, M. / Hirose, Y. / Fukui, K. | British Library Conference Proceedings | 1998


    Tailored blanks of high strength steel sheet - weldability and formability

    Uchihara,M. / Hirose,Y. / Fukui,K. et al. | Kraftfahrwesen | 1998