The natural rubber/styrene butadiene rubber/organoclay (NR/SBR/organoclay) nanocomposites were successfully prepared with different types of organoclay by direct compounding. The optimal type of organoclay was selected by the mechanical properties characterization of the NR/SBR/organoclay composites. The series of NR/SBR/organoclay (the optimal organoclay) nanocomposites were prepared with various organoclay contents loading from 1.0 to 7.0 parts per hundreds of rubber (phr). The nearly completely exfoliated organoclay nanocomposites with uniform dispersion were confirmed by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The results of mechanical properties measurement showed that the tensile strength, tensile modulus, and tear strength were improved significantly when the organoclay content was less than 5.0 phr. The tensile strength and the tear strength of the nanocomposite with only 3.0 phr organoclay were improved by 92.8% and 63.4%, respectively. It showed organoclay has excellent reinforcement effect with low content. The reduction of the score and cure times of the composites indicated that the organoclay acted as accelerator in the process of vulcanization. The incorporation of a small amount of organoclay greatly improved the swelling behavior and thermal stability, which was attributed to the good barrier properties of the dispersed organoclay layers. The outstanding performance of co-reinforcement system with organoclay in the tire formulation showed that the organoclay had a good application prospect in the tire industry, especially for the improvement of abrasion resistance and the reduction of production cost.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Preparation, characterization, and application of NR/SBR/Organoclay nanocomposites in the tire industry


    Beteiligte:
    Shan, Chunpeng (Autor:in) / Gu, Zheng (Autor:in) / Wang, Li (Autor:in) / Li, Peiyao (Autor:in) / Song, Guojun (Autor:in) / Gao, Zhenbin (Autor:in) / Yang, Xiaoyu (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2011


    Format / Umfang :

    10 Seiten, 9 Bilder, 5 Tabellen, 45 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Accessing Exfoliation in Organoclay - Polymer Nanocomposites

    Balogh, M. / Eckel, D. / Fasulo, P. et al. | British Library Conference Proceedings | 2002


    IMECE2002-33552 Structures and Characterization of Organoclay-Epoxy-Vinylester Nanocomposites

    Hussain, F. / Dean, D. / Haque, A. et al. | British Library Conference Proceedings | 2002


    Molecular dynamics of silica and organoclay filled XNBR nanocomposites

    Fritzsche,J. / Klueppel,M. / Deutsches Inst.f.Kautschuktechnologie,Hannover,DE | Kraftfahrwesen | 2009



    Application of NMR in the tire industry

    Herrmann,V. / Unseld,K. / Boehner,T. et al. | Kraftfahrwesen | 2004