Environmentally assisted crack growth mechanisms affecting the external surface of API X-60 pipeline steel has been investigated. Low frequency cyclic tests at 4.63x10-4 Hz were conducted in simulated groundwater (NS4 solution) under near neutral (pH approx. 7) conditions, similar to those for buried natural gas pipelines. The crack morphology and amount of growth were determined for two stress ratios, R (minimum/maximum stress) 0.5 and 0, at Kmax=25.5 MPa root of m under both constant and variable amplitude loading conditions. Examination of environmentally assisted crack was carried out using optical, scanning electron, focused ion beam and transmission electron microscopy. Transgranular stress corrosion cracking occurred at the higher R-ratio of 0.5. The crack was relatively wide, filled with corrosion product. By contrast, corrosion fatigue had taken place at R=0. The crack was also transcrystalline. Its tip was extremely sharp, and the amount of growth was greater. For the sample subjected to variable amplitude loading conditions, the crack was less sharp, but significantly sharper than that of the sample under constant load at R=0.5. The crack was open in many places, and the majority of the crack path was transgranular. Applying the superposition model to the variable amplitude test showed that the stress corrosion cracking growth rate accelerated when a single cycle at R=0 was combined with 159 cycles at R=0.5.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Environmental cracking of X-60 pipeline steel


    Weitere Titelangaben:

    Umgebungsbedingte Rissbildung am Pipelinestahl X-60


    Beteiligte:
    Plumtree, Alan (Autor:in) / Gu, Gordon Ping (Autor:in) / Li, Jian (Autor:in) / Liu, Pei (Autor:in) / Zavadil, Renata (Autor:in)


    Erscheinungsdatum :

    2010


    Format / Umfang :

    11 Seiten, 7 Bilder, 1 Tabelle, 7 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch