The efficiency of corrosion inhibitors may be reduced in the presence of corrosion product films. In the present paper the relation between surface wettability, corrosion rate and inhibitor performance was investigated on carbon steel specimens with partly protective ferrous carbonate (FeCO3) films in brine/oil mixtures. Two inhibitor base chemicals and a generic model compound were tested. The corrosion and inhibition tests were performed at 60 deg C in 3% NaCl brine under 1 bar CO2. Wettability was studied by contact angle measurements on steel coupons with iron carbonate films. In absence of oil, the inhibitors had no significant effect on the corrosion rate. The presence of oil significantly enhanced the performance of some of the tested inhibitors. The addition of the inhibitors leads to a significant change in wettability of FeCO3 for an originally oil-wet surface. For an initially water-wet surface, the FeCO3 remained hydrophilic when inhibitors were added. It was concluded that the main effect of oil is to modify the structure of the inhibitor film.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Interaction of carbon dioxide corrosion inhibitors with corrosion products deposit


    Weitere Titelangaben:

    Wechselwirkung der Korrosionsinhibitoren für die CO2-Korrosion mit den Ablagerungen der Korrosionsprodukte


    Beteiligte:
    Foss, Martin (Autor:in) / Gulbrandsen, Egil (Autor:in) / Sjöblom, Johan (Autor:in)


    Erscheinungsdatum :

    2008


    Format / Umfang :

    19 Seiten, 12 Bilder, 1 Tabelle, 40 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch