Hydrogen-induced cracking (HIC) and sulfide stress cracking (SSC) susceptibility of the submerged arc welded API 5L-X70 pipeline steel with different amounts of titanium at two levels of manganese (1.4% and 2%) were studied. The centerline segregation region (CSR) observed in the X70 pipe steel played an important role in the HIC susceptibility. Increased acicular ferrite content in the microstructure improved HIC resistance and SSC resistance, while bainite and martensite/austenite constituents deteriorated the workability of the welded specimens in sour environments. The 2% Mn-series welds showed higher SSC susceptibility than the 1.4% Mn-series welds due to the higher hardness values of the welds. The precipitated titanium carbonitrides in the welds can act as beneficial hydrogen traps and delay cracking in hydrogen sulfide environments. By further addition of titanium, the appearance of bainite and martensite/austenite in the microstructure outweigh any beneficial effect of titanium carbonitrides. The weld metals contained high percentage of acicular ferrite and good distribution of titanium carbonitrides yielded the best performance in sour environments. In two series of the welds, the best sour service properties were obtained at two compositions, 1.40% Mn-0.08% Ti and 1.92% Mn-0.02% Ti.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effects of alloying elements and microstructure on the susceptibility of the welded HSLA steel to hydrogen-induced cracking and sulfide stress cracking


    Beteiligte:
    Beidokhti, B. (Autor:in) / Dolati, A. (Autor:in) / Koukabi, A.H. (Autor:in)


    Erscheinungsdatum :

    2009


    Format / Umfang :

    7 Seiten, 44 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Effect of line pipe steel microstructure on susceptibility to sulfide stress cracking

    Koh, S.U. / Kim, J.S. / Yang, B.Y. et al. | Tema Archiv | 2004




    Hydrogen-induced cracking of steels under wet hydrogen sulfide environment

    Miyoshi, E. / Tanaka, T. / Terasaki, F. | Tema Archiv | 1975


    Resistance of products made of steel 20GL to sulfide stress corrosion cracking

    N. M. Blazhnov / E. A. Borisenkova / M. V. Khardin | DOAJ | 2023

    Freier Zugriff