Fatigue crack growth behaviour of two varieties of HSLA steels used in naval structural applications have been evaluated in air and 3.5% NaCl solution. The as-received heat treatment consisted of a spray quenching after austenitizing at 1330 K, followed by tempering at 833 K for 1h. In air both the HSLA steels showed similar resistance to fatigue crack growth. However, in 3.5% NaCl, the fatigue crack growth resistance of HSLA-80 steel was superior to that of HSLA-100. The apparent inferiority of HSLA-100 to corrosion fatigue crack growth resistance is attributed to rapid film formation and rupture, and occurrence of planar modes of failure. Effect of R-ratio on air fatigue and corrosion fatigue crack growth behaviour is rationalised by the concept of crack closure. Effect of cyclic frequency on corrosion fatigue behaviour is examined. It is noted that the mechanism of corrosion fatigue crack growth for the two HSLA steels changes with attendant change in the Paris slope. This leads to increase or decrease of crack growth rates, depending up on the delta K range of interest.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion fatigue crack growth behaviour of naval steels


    Weitere Titelangaben:

    Risswachstum bei Korrosionsermüdung von Schiffsbaustählen


    Beteiligte:
    Sivaprasad, S. (Autor:in) / Tarafder, S. (Autor:in) / Ranganath, V.R. (Autor:in) / Tarafder, M. (Autor:in) / Ray, K.K. (Autor:in)

    Erschienen in:

    Corrosion Science ; 48 , 8 ; 1996-2013


    Erscheinungsdatum :

    2006


    Format / Umfang :

    18 Seiten, 17 Bilder, 2 Tabellen, 50 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Near threshold fatigue crack growth in structural steels

    Rudd, W.J. / Booth, G.S. | Tema Archiv | 1998


    Fatigue Crack Growth Rate Testing of Two Structural Steels

    Walker, H. / Dowling, N. E. | SAE Technical Papers | 1979


    Fatigue crack growth rate testing of two structural steels

    Dowling,N.E. / Walker,H. / Westinghouse Res.and Dev.Cent.,Pittsburgh,US | Kraftfahrwesen | 1979


    Fatigue crack growth rate testing of two structural steels

    Dowling, N.E. / Walker, H. | Tema Archiv | 1979