Until now, to satisfy both requirements of the high tensile properties and the low temperature toughness, thick-walled X-80 and greater grade line pipes were developed by plate-UOE pipe manufacturing process. These were introduced bainite single phase transformed at very low temperature with ultra low carbon steels to keep coarse hard secondary phase away to improve the toughness. On the other hand, by hot rolled sheet to ERW (electric resistance welding) pipe manufacturing process, X-80 line pipe steel with bainitic microstructure made by low stop-cooling temperature was also studied. The ERW process can gain higher production rates, however, it was difficult to obtain bainite microstructure with good toughness because coiling process is indispensable. In hot rolling, stop-cooling is necessary before coiling at 500 - 700 deg C generally. The stop-cooling temperature of hot rolled sheet is very higher than that of plate, which is less than 350 deg C. So it was difficult to obtain good toughness by the lower bainite microstructure as same as the plate-UOE processed pipes by the ERW process. In this paper, solution of above issue was studied and a new microstructure for X-80 ERW line pipes, which has precipitation hardened bainitic ferrite microstructure, with low Pcm value for good weldability was developed. It was achieved that reduction of carbon content to the extremely low level causes excellent low temperature toughness.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Development of API X-80 grade electric resistance welding line pipe with excellent low temperature toughness


    Weitere Titelangaben:

    Entwicklung von widerstandsgeschweißten Leitungsrohren der Güte API X-80 mit ausgezeichneter Tieftemperaturzähigkeit


    Beteiligte:
    Nakata, Hiroshi (Autor:in) / Kami, Chikara (Autor:in) / Shiotani, Osamu (Autor:in) / Matsushita, Muneo (Autor:in) / Kawamura, Shuji (Autor:in)


    Erscheinungsdatum :

    2005


    Format / Umfang :

    7 Seiten, 12 Bilder, 2 Tabellen, 4 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch




    Experimental Research on Fracture Toughness of High Grade Line Pipe

    Xiong, Qing-Ren / Zhang, Jian-Xun / Feng, Yao-rong et al. | Tema Archiv | 2012


    Development of high toughness X70 grade clad steel pipe for natural gas transportation pipelines

    Kayano, Rinzo / Nitta, Yukio / Sato, Shinya et al. | Tema Archiv | 2007


    Electric welding of pipe

    Blodgett, O. | Engineering Index Backfile | 1947


    Development of high strength material and pipe production technology for grade X120 line pipe

    Hillenbrand, Hans-Georg / Biermann, Karin / Liessem, Andreas et al. | Tema Archiv | 2004


    FEED OIL PIPE EXHIBITING EXCELLENT SALT CORROSION RESISTANCE

    URASHIMA HIROSHI / SAKAMOTO SHUNJI / TERAOKA SHINICHI et al. | Europäisches Patentamt | 2019

    Freier Zugriff