Thermal shocks and temperature gradients associated with large thickness constitute difficult loadings for structures integrity analysis. Moreover, at low temperature or because of irradiation effects, the pressure vessel steel 16MND5 undergoes a transition in fracture mode which may lead to cleavage initiation. The prevention of this fracture mode is generally ensured by first staying outside the brittle domain and secondly, by imposing a stress intensity factor below the fracture toughness which is determined from monotonic and isotherm standard tests. But, with various temperature - loading histories, this criterion is not faultless. Therefore, in order to study in detail rupture under thermal shocks, with several loading types (mechanical and/or thermal loadings), a specific-adapted cracked ring has been developed. It consists of a 50mm thick ring which has a crack on the external diameter and several holes through the specimen to locally heat the ring by injecting hot water which can lead to crack initiation. This particular test allows the study of crack initiation with only thermal loading or both thermal loading and external mechanical loading. This article describes in details several tests including one with cleavage rupture. Moreover, numerical calculations are presented to estimate the mechanical fields at the crack tip and the global fracture mechanics parameters as a function of the temperature. Several rupture criteria are then applied to predict the initiation.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Tests and numerical analysis of cracked rings under thermal shock in the brittle / ductile transition of a pressure vessel steel.


    Beteiligte:
    Reytier, M. (Autor:in) / Chapuliot, S. (Autor:in) / Ferry, L. (Autor:in) / Nedelec, M. (Autor:in)


    Erscheinungsdatum :

    2005


    Format / Umfang :

    7 Seiten, 12 Bilder, 3 Tabellen, 7 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Ductile to brittle transition speed during ice indentation tests

    Sodhi, D. / Takeuchi, T. / Nakazawa, N. et al. | British Library Conference Proceedings | 1999


    Brittle to Ductile Transition in Ice under Tension

    E. M. Schulson / P. N. Lim / R. W. Lee | NTIS | 1984


    Relation between the Fatigue and Fracture Ductile-Brittle Transition in S500 Welded Steel Joints

    Sallaba, Finn / Rolof, Franziska / Ehlers, Sören et al. | Deutsches Zentrum für Luft- und Raumfahrt (DLR) | 2022

    Freier Zugriff

    Charpy Impact Fracture Energy and Ductile-Brittle Transition Temperature of Dual-Phase 590 Steel

    Ward, J. D. / Sands, R. G. / Chao, Y. J. | SAE Technical Papers | 2005