In the paper corrosion of iron (99.95%) and iron-chromium alloys (1-5% Cr) were investigated by mass loss and ac impedance. These low-chromium content alloys have been proposed as an intermediate corrosion-performance material between C-steel and stainless steels to be used in oil plants. It was observed that small contents of chromium in the alloy decrease the corrosion attack only in very specific pH range 4 < pH < 5. In CO2 medium, mass loss showed a linear behaviour with respect to time whereas in the presence of acetate the results were not monotonic. The effect of chromium is not important when the pH increases. By ac impedance, it was found that R-1 ind pand R-1 ind t vary proportionally with respect to mass loss. A discussion concerning the online monitoring of the corrosion rate is presented.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Corrosion rate of iron and iron-chromium alloys in CO2 medium


    Weitere Titelangaben:

    Korrosionsgeschwindigkeit von Eisen und Eisen-Chrom-Legierungen in CO2-haltiger Lösung


    Beteiligte:
    Carvalho, D.S. (Autor:in) / Joia, C.J.B. (Autor:in) / Mattos, O.R. (Autor:in)

    Erschienen in:

    Corrosion Science ; 47 , 12 ; 2974-2986


    Erscheinungsdatum :

    2005


    Format / Umfang :

    13 Seiten, 7 Bilder, 4 Tabellen, 38 Quellen