Pitting corrosion and structure characteristics of carbon dioxide (CO2) corrosion products on N80, 1 Cr, and 4Cr steel were studied. The results indicated that Cr-containing steels can suppress pitting corrosion effectively. While the Cr content in the matrix reached 4%, no pitting corrosion appeared on 4Cr steel. Cr existed mainly as amorphous compound Cr(OH)3 in corrosion products. With the improvement of Cr content in the steel matrix, the content of Cr(OH)3 in corrosion products increased remarkably, which could not only reduce the electrical conductivity of corrosion products but could also improve the cation selectivity of corrosion products. These two factors could improve the pitting resistance of Cr-containing steels.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of chromium on the pitting resistance of oil tube steel in a carbon dioxide corrosion system


    Weitere Titelangaben:

    Einfluss von Chrom auf den Lochfraßwiderstand von Rohrstahl für Öl in einem Kohlendioxid-Korrosionssystem


    Beteiligte:
    Chen, C.F. (Autor:in) / Lu, M.X. (Autor:in) / Sun, D.B. (Autor:in) / Zhang, Z.H. (Autor:in) / Chang, W. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 61 , 6 ; 594-601


    Erscheinungsdatum :

    2005


    Format / Umfang :

    8 Seiten, 6 Bilder, 5 Tabellen, 21 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Enhancement of pitting corrosion resistance of drawn aluminium tube

    Morley,E.J. / Post,C. / Hydro Aluminium Heat Transfer Toender,DK | Kraftfahrwesen | 1999


    Enhancement of pitting corrosion resistance of drawn aluminium tube

    Morley, E. J. / Post, C. / IMechE| SAE | British Library Conference Proceedings | 1999


    Pitting corrosion in pipeline steel weld zones

    Chaves, Igor A. / Melchers, Robert E. | Tema Archiv | 2011