The comprehensive properties of wheel steel for high speed train with carbon content from 0.4% to 0.7% were studied. As a result of increased carbon content, the abrasion resistance and contact fatigue durability of the test steel is increased, in the mean time, its impact toughness and thermal fatigue resistance is decreased. The test steel with 0.5%C and a small amount of microalloyed element has better comprehensive properties after 880 deg C normalizing and 530 deg C tempering, including better thermal fatigue resistance, higher contact fatigue durability, and proper abrasion resistance Thus the steel is suitable for produce high speed train wheel with higher resistance on fatigue damage such as spalling.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of carbon content on comprehensive properties of wheel steel for high speed train


    Weitere Titelangaben:

    Einfluss des Kohlenstoffgehalts auf die Gebrauchseigenschaften eines Stahls für die Räder von Hochgeschwindigkeitszügen
    Titel chinesisch


    Beteiligte:
    Ji, Huai-zhong (Autor:in) / Cui, Yin-hui (Autor:in) / Su, Hang (Autor:in) / Zhang, Yong-quan (Autor:in) / Shui, Heng-yong (Autor:in)

    Erschienen in:

    Iron and Steel, Peking ; 40 , 2 ; 62-81


    Erscheinungsdatum :

    2005


    Format / Umfang :

    5 Seiten, 4 Bilder, 2 Tabellen, 4 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Unbekannt




    Key technologies on high speed comprehensive inspection train

    Xiong, Kang / Weidong, Wang / Hailang, Li | IuD Bahn | 2013


    Wheel–rail wear progression of high speed train with type S1002CN wheel treads

    Gan, Feng / Dai, Huanyun / Gao, Hao et al. | Tema Archiv | 2015


    Wheel wear prediction on a high-speed train in China

    Li, Yuyi / Ren, Zunsong / Enblom, Roger et al. | Taylor & Francis Verlag | 2020



    Train wheel assembly and train

    YU CHANGYING / BAO XIAOKUN / WU JIAOJIAO et al. | Europäisches Patentamt | 2023

    Freier Zugriff