The effect of boron addition on the toughness and microstructure of seam weld metal was investigated in tensile strength range from 700 to 1100 MPa. Two types of weld metal were produced in this study. Type A weld metal was produced with boron added through the flux. Type B weld metal was produced by boron free flux. In the tensile strength range less than 800 MPa, type B weld metal showed lower absorbed energies than type A because of grain boundary ferrite formation. In the tensile strength range of 800 MPa or more, type B weld metal showed greater absorbed energies than type A. In this tensile strength range, some acicular ferrite is replaced with bainite or bainite/martensite and the absorbed energy decreases with increasing tensile strength. The type B weld metal had more acicular ferrite and greater absorbed energy than type A in this tensile strength range.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of boron addition on the toughness and the microstructure of high strength linepipe seam weld metals


    Beteiligte:
    Komizo, Yu-ichi (Autor:in) / Hamada, Masahiko (Autor:in) / Okaguchi, Shuji (Autor:in)


    Erscheinungsdatum :

    2004


    Format / Umfang :

    6 Seiten, 7 Bilder, 1 Tabelle, 17 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Characterisation of ultra high strength linepipe

    Ohm, R.K. / Martin, J.T. / Orzessek, K.M. | Tema Archiv | 2000



    Allowable strains for high strength linepipe

    Hohl, G.A. / Vogt, G.H. | Tema Archiv | 1992


    Development of high strength linepipe steel

    Yoo, Janq-Yong / Seo, Dong-Han / Ahn, Seong-Soo et al. | Tema Archiv | 2008