In view of the pressing need for improvements in space mechanisms and tribology research work, a thermal high-vacuum mechanism test facility has been constructed at Rome 'La Sapienza' University. The purpose of this facility is to provide fundamental data on the performance of mechanical components and materials in high vacuum in order to test the validity of space mechanism designs. The facility also makes it possible to examine the behaviour of both mechanisms and materials under combined environmental factors, such as ultraviolet radiation, atomic oxygen and temperature. This paper reports on the behaviour of titanium recirculating ball screws provided by Umbra Cuscinetti SpA (Foligno, Italy) under thermal-vacuum conditions. It is to be noted that these ball screws - well known in the aeronautical field - may be particularly attractive as a new generation of space mechanisms. A solid multilayer film of tungsten carbide/carbon (WC/C) was deposited on screw surfaces as a lubricant and was then compared with the case of no lubrication, which presently appears promising for many mechanisms. In order to compare experimental results, traditional stainless steel mechanisms were also tested and analysed. The requisites imposed by the space environment, as well as by contact mechanical stresses, have given useful information on a preliminary geometrical configuration and choice of materials, both of which are presented in this paper. Thermal-vacuum effects on overall ball screw efficiency and on ball screw coating friction and wear are also reported and commented on herein as well as numerical contact simulations of crack mechanisms.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Structural behaviour of aeronautical tungsten carbide/carbon-coated titanium ball screws under space thermal-vacuum conditions


    Beteiligte:
    Corradi, Sandro (Autor:in) / Marchetti, M. (Autor:in)


    Erscheinungsdatum :

    2005


    Format / Umfang :

    11 Seiten, 12 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    TUNGSTEN CARBIDE POWDER Cobalt Coated

    SAE Technical Papers | 2011


    Tungsten Carbide Powder, Cobalt Coated

    SAE Technical Papers | 2002


    TUNGSTEN CARBIDE POWDER Cobalt Coated

    SAE Technical Papers | 1994


    TUNGSTEN CARBIDE POWDER Cobalt Coated

    SAE Technical Papers | 1971