THE CORROSION behaviour of titanium and titanium alloy Ti-6Al-4V in a deep-sea environment the Indian Ocean is presented. For the first time, coupons of these materials were exposed for longer duration at great depth in the ocean. Weight-loss measurements did not show any corrosion of the titanium or the alloy at depths of 500, 1200, 3500, and 5100m. Tensile tests were carried out on the deep-sea exposed speciments, and were compared with unexposed control specimens. The results show that the tensile strength did not change after deep-sea exposure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A deep-sea corrosion study on titanium and Ti6Al4V alloy


    Beteiligte:
    Venkatesan, R. (Autor:in) / Dwarakadasa, E.S. (Autor:in) / Ravindran, M. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2004


    Format / Umfang :

    6 Seiten, 11 Quellen



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Characterization of Titanium Alloy (Ti6Al4V) Obtained by Additive Manufacturing

    Da Silva, Jorge Vicente Lopes / Santiago, Rafael Celeghini / Da Fonseca Brasil, Reyolando Lopes Rebello et al. | SAE Technical Papers | 2020


    Modelling and Simulation of Surface Roughness during the Turning Operation of Titanium Alloy (Ti6Al4V)

    Daniyan, Ilesanmi / Fameso, Festus / Mpofu, Khumbulani et al. | IEEE | 2022




    Behavior of the Weldment Corrosion of Titanium and Titanium Alloy

    Chui, W. / Sun, Q. / Wei, H. et al. | British Library Conference Proceedings | 1994