The work presented in this paper focuses on the effect of the presence of non-equilibrium delta-ferrite on the impact properties of a supermartensitic stainless steel. To generate homogeneous delta-ferrite containing microstructures the material was subjected to a series of high temperature furnace heat treatments. Three microstructures possessing variable ferrite content and different grain sizes were generated. Charpy impact results indicate that the presence of 14% delta-ferrite in a martensitic matrix of 60 micron prior austenite grain size, raises the ductile to brittle transition temperature (DBTT) by about 50 C deg compared with a fully martensitic microstructure of 80 micron. For a similar grain size, reducing the amount of delta-ferrite from 14 to 2% restored the DBTT to a level comparable to that of the tempered parent material. A Gleeble simulator was used to create the range of microstructures found in a weld heat affected zone (HAZ). Testing of the simulated HAZ indicated that toughness was not significantly affected by the presence of delta-ferrite. The DBTT was comparable to that of the parent material and lower than that of the heat treated specimens containing 14% delta-ferrite.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of delta-ferrite on impact properties of supermartensitic stainless steel heat affected zones


    Beteiligte:
    Carrouge, D. (Autor:in) / Bhadeshia, H.K.D.H. (Autor:in) / Woollin, P. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2004


    Format / Umfang :

    13 Seiten, 26 Bilder, 8 Tabellen, 21 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Welding consumables for supermartensitic stainless steels

    Gough, P.C. / Farrar, J.C.M. / Zhang, Z. | Tema Archiv | 1999



    Moderate cathodic protection of supermartensitic stainless steels

    Ligier, V. / Pourbaix, A. / Carpentiers, P. | Tema Archiv | 2000