Various methods of thermal shock testing are used by aircraft and industrial gas turbine engine (IGT) manufacturers to characterize new thermal barrier coating systems in the development stage as well as for quality control. The cyclic furnace oxidation test (FCT), widely used in aircraft applications, stresses the ceramic/bondcoat interface, predominantly through thermally grown oxide (TGO) growth stress. The jet engine thermal shock (JETS) test, derived from a burner rig test, creates a large thermal gradient across the thermal barrier coating (TBC), as well as thermomechanical stress at the interface. For IGT applications with long high-temperature exposure times, a combination of isothermal preoxidation and thermal shock testing in a fluidized bed reactor may better represent the actual engine conditions while both types of stress are present. A comparative evaluation of FCT, JETS, and a combined isothermal oxidation and fluidized bed thermal shock test has been conducted for selected ceramic/bondcoat systems. The results and the failure mechanisms as they relate to the TBC system are discussed. A recommendation on the test method of choice providing best discrimination between the thermal shock resistance of the ceramic layer, the ceramic/bondcoat interface, and even substrate related effects, is given.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Thermal shock testing of thermal barrier coating/bondcoat systems


    Beteiligte:
    Bolcavage, Ann (Autor:in) / Feuerstein, Albert (Autor:in) / Foster, John (Autor:in) / Moore, Peter (Autor:in)


    Erscheinungsdatum :

    2004


    Format / Umfang :

    9 Seiten, 5 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Preparation and Thermal Shock Performance of ZrO2/NiCrAlY Thermal Barrier Coating

    WANG Lingshuang / CAO Guojian / TANG Guangze et al. | DOAJ | 2017

    Freier Zugriff

    Enhanced zirconia thermal barrier coating systems

    Clarke, D. | Online Contents | 2006


    HITS - High Insulation Thermal Barrier Coating systems

    Saint-Ramond, Bertrand | Online Contents | 2001


    Thick thermal barrier coating ( TTBCs )

    Beardsley,M.B. / Caterpillar,US | Kraftfahrwesen | 1995