Al-Mg-Si alloy extrusions and rolled Al-Mg alloy sheets used for car body frames and panel components are welded with high-power Nd: YAG lasers and the joint performance compared with those of MIG welding and resistance spot welding for the same parts. Joint strength and welding distortion were also evaluated. The results obtained may be summarised as follows: (1) During lap welding of thin Al-Mg and Al-Mg-Si alloy sheets with a twin-spot Nd: YAG laser, lap joints with a stable high strength are obtained over a wide welding speed range at a beam distance of 0.6 mm. (2) Laser welding can be performed at an approximately 10-fold faster speed than MIG welding. The amount of welding distortion then found can be substantially reduced. (3) Laser stitch welding provides the smallest distortion. (4) The laser weld bead length with strength equivalent to one resistance spot weld is around 14 mm.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Welding of aluminium car body parts with twin-spot high-power Nd: YAG laser


    Beteiligte:
    Shibata, K. (Autor:in) / Iwase, T. (Autor:in) / Sakamoto, H. (Autor:in) / Kasukawa, M. (Autor:in)

    Erschienen in:

    Welding International ; 17 , 12 ; 939-946


    Erscheinungsdatum :

    2003


    Format / Umfang :

    8 Seiten, 17 Bilder, 3 Tabellen, 8 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Spot-Welding Gun With Pivoting Twin-Collet Assembly

    Nguyen, Francis / Simpson, Gareth / Hoult, William S. | NTRS | 1996


    Laser spot welding of electronic micro parts [5662-48]

    Ostendorf, A. / Temme, T. / Zeadan, J. et al. | British Library Conference Proceedings | 2004



    The gap tolerance in CO2 twin-spot laser tailored blank welding

    Hsu,R. / Engler,A. / Heinemann,S. et al. | Kraftfahrwesen | 1999


    High power Nd: YAG laser welding of aluminium alloys for car body

    Shibata, K. / Sakamoto, H. / Iwase, T. et al. | Tema Archiv | 2000