Characterization studies with focus on the weld metal of a two-sided submerged arc production weld in an x70 HLSA line-pipe steel were carried out. A two-sided single pass laboratory weld was made using the same set of materials and consumables, and was compared with the production weld. All the welds were tested for their chemical composition, weld profile, microstructure, strength, microhardncss and Charpy impact toughness. Similarities and differences in welding conditions are outlined. A laboratory weld comparable to the production weld was obtained. It demonstrated higher toughness than the production weld at all test temperatures due to lower percentage of grain boundary phases. Inclusions with diameters between 0.5 and 0.7 micron improve the low temperature impact properties of the weld metal. The inside diameter weld has higher impact properties as compared with the outside diameter weld because of heat treatment imparted by the latter. The weld metal region was stronger and harder than the base metal and heat affected zone.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Characterization and comparison of spirally welded HSLA steel line-pipe submerged arc production weld and a laboratory weld


    Beteiligte:
    Nemade, J.B. (Autor:in) / Bhole, S.D. (Autor:in)


    Erscheinungsdatum :

    2003


    Format / Umfang :

    15 Seiten, 10 Bilder, 6 Tabellen, 16 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Datenträger


    Sprache :

    Englisch




    Coatings for pipe line weld field joints

    Goff, B.C. | Tema Archiv | 1990


    Assessing offshore submerged arc weld metals

    Murray, A. / Norrish, J. / Billingham, J. | Tema Archiv | 1996


    Test measures ERW line pipe weld ductility

    Williams, D.N. / Eiber, R.J. | Tema Archiv | 1985



    Laser Weld Process Monitoring in Production of Tailor-Welded Blanks

    Walters, C. T. / Ream, S. L. / Laser Institute of America | British Library Conference Proceedings | 1996