Metallized Teflon PEP (fluorinated ethylene propylene ), a common spacecraft thermal control material, which forms the exterior layer of the Hubble Space Telescope (HST) has become embrittled and suffers from extensive cracking. Teflon samples retrieved during Hubble servicing missions and from the Long Duration Exposure Facility (LDEF) indicate that there may be continued degradation in the tensile properties over time. An investigation has been conducted to evaluate the effect of air and vacuum storage on the mechanical properties of x-ray exposed PEP. Aluminized-PEP (Al-PEP) tensile samples were irradiated with 15.3 kV Cu x-rays and stored in air or under vacuum for various time periods. Tensile data indicate that samples stored in air display larger decreases in their tensile properties than for samples stored under vacuum. Air-stored samples developed a hazy appearance, which corresponded to a roughening of the aluminized surface. Optical property changes were also characterized. These findings indicate that air exposure plays a role in the degradation of irradiated PEP, therefore proper sample handling and storage is necessary with materials retrieved from space.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Effect of air and vacuum storage on the tensile properties of X-ray exposed aluminized-FEP


    Beteiligte:
    Groh, K.K. de (Autor:in) / Gummow, J.D. (Autor:in)


    Erscheinungsdatum :

    2001


    Format / Umfang :

    11 Seiten, 10 Bilder, 4 Tabellen, 15 Quellen




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    Aluminized Coatings

    Thomson, A.G. | Emerald Group Publishing | 1954


    Heat Resistant Aluminized Paint

    SAE Technical Papers | 2015


    Improved Aluminized Multilayer Insulation

    Tepper, Edward H. | NTRS | 1988


    Properties of Aluminized Steels for Hot-Forming

    Maki, Jun / Kusumi, Kazuhisa / Ohgami, Masahiro et al. | SAE Technical Papers | 2003