The landing gear of an aircraft failed during landing due to the fracture of its outer cylinder attachment lug, which is manufactured from an aluminium alloy following Britisch Specification DTD 5104 A. The material presented an oriented microstructure composed of bands of recrystallized and unrecrystallized grains. The unrecrystallized areas showed intense intragranular precipitacion, while the recrystallized areas presented large primary precipitates and fine intergranular precipitation. Pit cavities associated with intergranular corrosion were observed along the perimeter line of the attachment bore surface and consumed preferentially the recrystallized areas of the microstructure. Fractographic examination revealed that the unstable crack propagation was originated in these stress raisers. The fracture mode is preponderantly ductile intergranular, with areas showing ductile fracture composed of small dimples. The results indicated that both corrosion and intergranular ductile crack propagation were favoured by the orientation of the microstructure, which was perpendicular to the free surface. Finally, the abnormal loads absorbed by the outer cylinder during the landing procedure associated with corrosion cavities located in a critical area may be concluded as the cause fir this failure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Aircraft landing gear failure: fracture of the outer cylinder lug


    Weitere Titelangaben:

    Versagen des Flugzeug-Bugfahrwerks: Bruch des Befestigungsauges am Außenzylinder


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    2002


    Format / Umfang :

    15 Seiten, 14 Bilder, 2 Tabellen, 19 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Aircraft landing gear outer barrel and landing gear with same

    WU BIN / WANG XIANGMING / XING BENDONG et al. | Europäisches Patentamt | 2020

    Freier Zugriff

    Hydraulic cylinder for aircraft landing gear

    KONDO TAKU / ONISHI TAKAAKI / HAGIHARA SHOGO | Europäisches Patentamt | 2019

    Freier Zugriff

    HYDRAULIC CYLINDER FOR AIRCRAFT LANDING GEAR

    KONDO TAKU / ONISHI TAKAAKI / HAGIHARA SHOGO | Europäisches Patentamt | 2021

    Freier Zugriff

    HYDRAULIC CYLINDER FOR AIRCRAFT LANDING GEAR

    KONDO TAKU / ONISHI TAKAAKI / HAGIHARA SHOGO | Europäisches Patentamt | 2017

    Freier Zugriff

    Manufacturing method of aircraft landing gear outer barrel

    XING BENDONG / WANG XIANGMING / WU BIN et al. | Europäisches Patentamt | 2020

    Freier Zugriff