High-cycle fatigue (HCF) failures in aircraft engines are attributed to material damage states, created during processing or by in-service loading and environmental conditions, and then propagated to failure by HCF loading. The loading configuration experienced by aircraft engine turbine blades consists of an axial load caused by the centrifugal acceleration during rotation combined with the tensile and compressive loads caused by the natural vibrations of the blades themselves. To simulate these loading conditions a new testing apparatus was developed that is capable of providing interactive low-cycle fatigue/high-cycle fatigue (LCF/HCF) loading, in ratios (of magnitude and frequency) that give a realistic simulation of the actual flight loads experienced by engine components. This testing apparatus is based on a HCF cell operating at 20 kHz. The cell can also be integrated to a servo-hydraulic load frame, which provides a second fatigue cycle. The objective of this study was to demonstrate the capabilities of the new HCF apparatus via thermographic measurements and by performing LCF/HCF interaction tests.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    A high-cycle fatigue apparatus at 20 kHz for low-cycle fatigue/high-cycle fatigue interaction testing


    Beteiligte:
    Matikas, T.E. (Autor:in)


    Erscheinungsdatum :

    2001


    Format / Umfang :

    11 Seiten, 19 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Fatigue Reliability Analysis for High Cycle Fatigue Regime

    Apetre, Nicole / Arcari, Attilio / Sarkar, Subhasis et al. | AIAA | 2012


    Fatigue Reliability Analysis for High Cycle Fatigue Regime

    Apetre, N. / Arcari, A. / Sarkar, S. et al. | British Library Conference Proceedings | 2012


    Low cycle fatigue testing facility

    BROWN, B. | AIAA | 1982


    Small Cracks and High-Cycle Fatigue

    Ritchie, R. O. | British Library Online Contents | 1996


    Crack Propagation of Compressor Blade on Low Cycle Fatigue Combined with High Cycle Fatigue

    Zheng, G. / Zhao, C. / Zhang, M. et al. | British Library Conference Proceedings | 1994