Crack-tip opening displacement (CTOD) fracture toughness measurements have been performed on longitudinal, through-wall thickness, three-point bend samples from an X-80 pipeline steel. Samples were subjected to cathodic protection in an Ns-4 test solution prior to and during fracture toughness determination. Variation of the precharge time and the crosshead speed for CTOD measurement indicated that precharge times > 7 days and crosshead speeds giving rates of increase of stress intensity factor < 0.2 MPa m0.5/s were required to obtain worst-case conditions. Under the worst-case conditions, the CTOD fracture toughness for the X-80 material was reduced by 75%, to nearly equal 0.17 mm, from a value of nearly equal 0.70 mm in air. This reduction in fracture toughness was found to be similar at pH values down to 2.5. Although the samples were not taken with the fracture in an orientation representative of a typical pipeline defect, the reduction in fracture toughness was representative of the behavior of X-80. Comparison with literature data for conventional pipeline steels indicates that they suffer a similar loss in fracture toughness under worst-case conditions. The level of fracture toughness reduction for high-strength steels is of greater concern because they will operate under higher stresses. However, tolerable defect size calculations indicate that hydrogen-induced stress cracking (HSC) will not be a failure mechanisms for X-80 steel parent material without some additional influence.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Variation of the fracture toughness of a high-strength pipeline steel under cathodic protection


    Weitere Titelangaben:

    Veränderung der Bruchzähigkeit von hochfestem Rohrstahl bei kathodischem Korrosionsschutz


    Beteiligte:
    Andrews, P. (Autor:in) / McQueen, M. (Autor:in) / Millwood, N. (Autor:in)

    Erschienen in:

    Corrosion, Houston ; 57 , 8 ; 721-729


    Erscheinungsdatum :

    2001


    Format / Umfang :

    9 Seiten, 8 Bilder, 4 Tabellen, 16 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Cathodic protection potential penetration under disbonded pipeline coating

    Jack, T.R. / Boven, G. van / Wilmott, M. et al. | Tema Archiv | 1994




    Fracture toughness parameter in a pipeline

    Al-Obaid, Y.F. | Tema Archiv | 1992