Oxidation protection is an integral part of any carbon/carbon aircraft brake friction material, since unprotected carbon oxidizes rather quickly at typical brake operating temperatures. Oxidation protection schemes are complicated by the environmental presence of numerous catalytic materials, typically alkali metal salts. P-13 antioxidant is a standard phosphoric acid based antioxidant which is used on commercial carbon/carbon friction materials. CABENIX 2400 material, a commercial carbon-carbon brake material, was used for all samples. Samples were immersion coated with antioxidant and then thermally cured. As in previous experiments multiple coatings significantly improved oxidation resistance for all formulations in both catalyzed and uncatalyzed environments. Addition of the KH2PO4 significantly improved resistance to catalytic oxidation.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Inhibition of catalytic oxidation in carbon-carbon composite friction materials


    Weitere Titelangaben:

    Unterbindung der katalytischen Oxidation von carbonfaserverstärktem Kohlenstoff als Reibwerkstoff


    Beteiligte:
    Walker, T.B. (Autor:in) / Booker, L.A. (Autor:in)


    Erscheinungsdatum :

    2000


    Format / Umfang :

    2 Seiten, 1 Bild, 2 Quellen



    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Carbon/carbon composite friction discs for aerospace

    Buchgraber, W. | Tema Archiv | 2003


    Carbon-carbon composite materials

    Savage, G. | Tema Archiv | 1988


    Pyrolytic carbon wet friction materials

    Awasthi,S. / Taccini,G. / Hitco Carbon Composites,US SGL Carbon,US | Kraftfahrwesen | 2005


    Pyrolytic Carbon Wet Friction Materials

    Taccini, G. / Awasthi, S. | SAE Technical Papers | 2005


    Development of Reduced Catalytically Active Runway Deicer Fluids for Carbon/Carbon Composite Friction Materials

    Steinke, D. J. / Johnson, K. L. / Walker, T. B. | SAE Technical Papers | 2002