The combined effects of four variables on calculated spectrum fatigue crack growth (FCG) in 7075-T73 aluminum were compared using an experimental design approach (NASGRO 3.0 adaptation). The four parameters considered were: (1) load interaction, (2) load sequence (rainflow counted low-to-high, rainflow counted and randomized, and rainflow counted high-to-low), (3) crack tip stress state (plane stress versus plane strain) and (4) spectrum type (FELIX-28 helicopter rotor blade spectrum versus F-16 wing-root-bending moment spectrum). Each of the three load-interaction models available in NASGRO 3.0 was used to compute load-interaction effects. The investigation concluded that the order of cycles and crack tip constraint play relatively minor roles in computed FCG for problems involving repeated application of either of the given spectra, while the effects of the spectrum type itself, inclusion of load-interaction effects and the synergy of spectrum with load interaction are highly significant.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Quantifying spectrum loading effects on fatigue crack growth in 7075-T73 aluminum


    Weitere Titelangaben:

    Quantifizierung der Auswirkung zeitabhängiger Belastung auf das Wachstum von Ermüdungsrissen in 7075-T73 Aluminium


    Beteiligte:
    Zion, H.L. (Autor:in) / Johnson, W.S. (Autor:in) / Ball, D.L. (Autor:in) / Everett, R.A. jun. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2000


    Format / Umfang :

    8 Seiten, 8 Bilder, 10 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch





    Nonplanar Fatigue Crack Growth in 7075-T73 Aluminum

    Forth, S. C. / Favrow, L. H. / Keat, W. D. et al. | British Library Conference Proceedings | 1999


    Fatigue crack growth from corrosion damage in 7075-T6511 aluminium alloy under aircraft loading

    DuQuesnay, D.L. / Underhill, P.R. / Britt, H.J. | Tema Archiv | 2003


    Study of Aluminum Alloy 7075-T6 under Ultrasonic Fatigue Loading

    Schichtel, Jacob J. / Datta, Siddhant / Chattopadhyay, Aditi | ASCE | 2022