Impact fracture in zone- and full-tempered glass was studied by high speed photography using a Cranz-Schardin type camera, and the following conclusions were reached: The maximum crack velocities of tempered glass were 1.500 x 103 m/s and 1.486 x 103 m/s for the tempering strengths of 172 MPa and 123 MPa, respectively. The result indicated weak dependence of the maximum velocity on the tempering strength. High-speed photoelastic color photography was successfully performed using a tint plate in the photoelastic optical setup. Change of dynamic stress distribution around the crack tip could be well visualized by the change in color. Fast cracks even with the terminal velocity can vertically turn quickly with a small curvature of 2 mm. About 70 % of the total secondary cracks developed within 1 msec after initiation of the impact crack. Caustic images were observed for thick tempered specimens and it was shown that the dynamic stress intensity factor of a crack with the terminal velocity decreases by 50 % recovered at a propagation distance of less than 20 mm.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Tempered vacuum glass

    ZHAO YAN / LI YANBING / LIANG XIPING et al. | Europäisches Patentamt | 2020

    Freier Zugriff

    Tempered glass breaking device

    ZHONG XINGYING | Europäisches Patentamt | 2015

    Freier Zugriff

    Transportation device for tempered glass

    LIANG ZHONGKUI | Europäisches Patentamt | 2021

    Freier Zugriff

    TEMPERED GLASS BREAKER FOR ESCAPE

    KIM DONG HYUN / OH JAE JIN / KWON HYUK KU et al. | Europäisches Patentamt | 2019

    Freier Zugriff

    APPARATUS FOR BREAKING TEMPERED GLASS

    CHOE HYUN DERK / PARK SEONG JE / LEE MIN SEONG | Europäisches Patentamt | 2022

    Freier Zugriff