The initial two-year study with full rotational motion (NADC-79137-60) was further extended with investigations under oscillatory motion to advance understanding of simultaneously occurring corrosion-wear phenomena in Navy aircraft components, and to use this knowledge to improve reliability in component performance. An additional corrosion-wear parameter, namely, coefficient of friction, was evaluated along with open-circuit potential, corrosion current density, and wear loss, which were statistically analyzed in terms of load, frequency, corrosion inhibitor, and lubricant, as well as run-in time. Corrosion-wear surface morphologies were examined with SEM and EDX, and surface roughness measurements were analyzed. The effect of wear on the corrosion process was very marked for alloys which were able to form a passive film. Disruption of the passive film was the principal factor leading to an increase in corrosion rate and wear loss, while surface deformation by increasing load and motion within the range evaluated appeared to be secondary. An increase in load at a constant frequency did not affect the polarization reaction processes as much as an increase in frequency at a constant load. It was clearly demonstrated that wear phenomena dominate the anodic polarization process, but not the cathodic polarization process.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Wear and corrosion of components under stress and subjected to motion


    Weitere Titelangaben:

    Verschleiss und Korrosion von Bauteilen unter Belastung bei gleichzeitigem Einfluss von Bewegung


    Beteiligte:
    Kim, K.Y. (Autor:in) / Bhattacharyya, S. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1984


    Format / Umfang :

    150 Seiten


    Medientyp :

    Report


    Format :

    Print


    Sprache :

    Englisch




    Corrosion-accelerated wear

    Young, H.J. | Engineering Index Backfile | 1933



    3P XYTREX wear components

    Online Contents | 2017


    Wear of machine components

    Kragelskii,I.V. / Marchenko,E.A. / Res.Inst.of Mech.Engng.,Moskau,SU | Kraftfahrwesen | 1982


    Wear and corrosion of rails

    Dearden, J. | Engineering Index Backfile | 1965