Acoustic Emission is a suited technique for the characterization of damage in composite materials, as also in metallic structures. A lot of test with different CFRP specimens make sure that there are correlations between certain AE parameters, respectively their variation, and characteristics of defects,which are typical for composites. The damage history of the test specimens can be analyzed with a very good chronological resolution. This includes an exact correlation between acoustic and mechanical parameters, such as load, cycle number etc. The present results demonstrate a potential for distinguishing between some dominant failure mechanisms, as fiber failure and matrix cracking, and noise generated by internal friction. Locating existing defects and tracking spatial damage progression is another field of application. All AE data are being monitored continuously-in situ - during loading the specimen. Post-test-analysis of the stored data with suited computer programs enables a more sophisticated evaluation.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Monitoring of defect progression by acoustic emission


    Weitere Titelangaben:

    Anzeige der Fehlerausbreitung durch Schallemissionanalyse


    Beteiligte:
    Block, J. (Autor:in)


    Erscheinungsdatum :

    1983


    Format / Umfang :

    11 Seiten, 10 Bilder, 1 Tabelle, 6 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    Influence of Fabric Architecture on Damage Progression Evidenced by Acoustic Emission Measurements

    Miller, David A. / Samborsky, Daniel / Cairns, Doug S. et al. | AIAA | 2016


    Acoustic Emission for Tank Bottom Monitoring

    Martin, Gary | Tema Archiv | 2013


    Acoustic emission for monitoring aircraft structures

    Holford, K.M. / Pullin, R. / Evans, S.L. et al. | Tema Archiv | 2009



    Acoustic emission for monitoring aircraft structures

    Holford, K M / Pullin, R / Evans, S L et al. | SAGE Publications | 2009