New ferritic stainless steels have been developed for use by the automobile industry. These steels demonstrate high resistance to pitting and a longer product lifetime can be expected, especially in 'chlorine type' environments. This report deals with the effects of alloying element on steels containing 16-19 % Cr, with special attention devoted to pitting resistance. It was observed that a small amount of Cu and Ni increased pitting resistance. A decrease in the S content of the steel led to an increase in the pitting resistance. The remarkable improvement in the rust staining resistance for this low S steel was confirmed by the CASS test. Based on results, 19 % Cr-0.5 % Cu-Ni(Nb)-low S ferritic stainless steels were selected. These steels 'NSS442M2' and 'NSS442M3' have excellent rust staining resistance in the accelerated tests. The atmospheric exposure test proved that the rust staining resistance of NSS442M2 and NSS442M3 was comparable to or greater than that of Type 304.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    New ferritic stainless steels for automotive trim application


    Weitere Titelangaben:

    Neue ferritische nichtrostende Staehle fuer Automobilausruestungen


    Beteiligte:
    Adachi, T. (Autor:in) / Kanamaru, T. (Autor:in)


    Erscheinungsdatum :

    1983


    Format / Umfang :

    20 Seiten, 19 Bilder, 4 Tabellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch




    New Ferritic Stainless Steels for Automotive Trim Application

    Adachi,T. / Kanamaru,T. / Nisshin Steel,JP | Kraftfahrwesen | 1983


    New Ferritic Stainless Steels for Automotive Trim Application

    Kanamaru, Takayoshi / Adachi, Toshiro | SAE Technical Papers | 1983


    Ferritic stainless steels for the automotive industry

    Maitrepierre, P. / Veyrac, P. de | Tema Archiv | 1988


    Development of ferritic stainless steels for automotive exhaust systems

    Alves, H.J.B. / Carvalho, J.A.N. / Aquino, M.V. et al. | Tema Archiv | 2002