The effect of water pressure on formation of porosity in underwater gravity welding were investigated within the range of 0 to 6 kgf/cm2 (gauge). The ilmenite type, high titanium oxide type and iron powder cm 2 iron oxide type electrodes of 4 mm in diameter and SM41 steel base metals of 6 and 9 mm in thickness are used. Main results are summarized as follows: The porosity is formed in weld metal, when water pressure is over about 0.5 kgf/cm2. The porosity increases with an increasing of water pressure. The porosity (A type) in weld metal obtained under water-pressure of 0.5 to 3 kgf/cm2 is caused by the concentrated hydrogen in front of the solidification front. The porosity (B type) is observed in weld metal obtained under water-pressure of 3 to 6 kgf/cm2 and the special solidification lines are often generated around porosity. The porosity is caused by bubble formed in molten metal, which is catched by the progressing solidification front. The special solidification line is formed by a repetition of growth of bubble at the progressing solidification front and escape of bubble from there. Changes of porosity shape and porosity formation mechanism with water pressure are caused by concentration of hydrogen in molten metal, which is greatly increased with water pressure.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    On formation of porosity in underwater weld metal - effect of water pressure on formation of porosity


    Weitere Titelangaben:

    Ueber die Bildung der Porositaet im Unterwasserschweissmetall - Einfluss des Wasserdrucks auf die Bildung der Porositaet
    Titel japanisch


    Beteiligte:
    Hasui, A. (Autor:in) / Suga, Y. (Autor:in) / Kurihara, M. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1981


    Format / Umfang :

    7 Seiten, 11 Bilder, 3 Tabellen, 9 Quellen


    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Japanisch




    Mechanisms of Porosity Formation in Aluminum Welds

    W. V. Mixon / D. D. Pollock / W. W. Reinhardt | NTIS | 1966


    Eliminating Porosity in the Weld Bead of Automotive Axles

    Maia, Ivan Gonçalves / Trevisan, Roseana da Exaltação | SAE Technical Papers | 2007


    Porosity Formation in Laser Welding of Tailored Blanks

    Ohara, Masahiro / Furusako, Seiji / Miyazaki, Yasurtobu | SAE Technical Papers | 2003



    Numerical Modeling of Pressure Drop Across High Porosity Metal Foams

    Bhattacharya, Anandaroop / Mahajan, Roop | AIAA | 2002