Recent studies have shown that the benefits gained by using graphite-epoxy composite structures may not be realized without some risk. The graphite fibers are very good electrical conductors and fibers released into the environment during a fire create a possible hazard to electrical equipment. Several graphite-epoxy hybrids were exposed to a fire and simulated explosion and their graphite fiber retention characteristics were examined. Several low melting -temperature glasses which wet and clump graphite-fibers and a glassgraphite fabric which reduced impact damage were identified as promising hybridizing components to minimize graphite fiber release. (DePo)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Effects of boron and glass hybrid expoxy-composites on graphite-fiber release in an aircraft fire


    Weitere Titelangaben:

    Wirkung von Borfaser- und Graphitfaser-Hybridepoxidverbundstoffen auf die Losloesung von Fasern bei Glugzeugbraenden


    Beteiligte:
    Tompkins, S.S. (Autor:in) / Brewer, W.B. (Autor:in)


    Erscheinungsdatum :

    1979


    Format / Umfang :

    11 Seiten, 15 Bilder, 1 Tabelle, 2 Quellen


    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Print


    Sprache :

    Englisch





    High thermal conductive expoxy resin composites with controlled higher order structures

    Fukushima,K. / Takahashi,H. / Hattori,M. et al. | Kraftfahrwesen | 2005


    Cycloaliphatic Expoxy Insulators - Experiences over 30 Years

    Massen, U. / Beisele, C. / Energietechnische Gesellschaft im VDE (ETG) | British Library Conference Proceedings | 1999


    Expoxy foam bonded metal for stiff structures

    Smith, C.I. / Brown, C.J. | Tema Archiv | 1999