In the present investigation, on 17 Cr ferritic oxide dispersion strengthened (ODS) steel composition of (430L + 0.3Y2O3 + 0.5ZrO2 + 0.1Ti) wt% (alloy A) and (430L + 0.3Y2O3 + 0.5ZrO2 + 0.1Ti + 4Al) wt% (alloy B) were developed through mechanical alloying (MA) using VHP (vacuum hot pressing). The mechanically alloyed powders were taken at different milling time intervals for confirming the nanocrystalline size using X-Ray Diffraction (XRD). Finally, 20 h of milled powders were consolidated through vacuum hot pressing (VHP) at 1180 °C in the pressure levels of 60 MPa, and the cooling rate of 50°C/min. Throughout the experiments, the vacuum level was maintained by 10−3 Torr. Hot-pressed samples were subjected to densification studies; microstructural examination and hardness were analyzed in the current study. The nanocrystalline size of 3.6 nm (alloy A) and 6 nm (alloy B) were obtained at 20 h of milling time. The highest hot-pressed density of 7.60 g/cc (99% theoretical density) was acquired for aluminium-free ferritic ODS steel (alloy A) pressure at 60 MPa, whereas aluminium-contained alloy B lesser hot-pressed density of 7.34 g/cc was obtained. The microstructures of alloy A and alloy B containing ferrite along with complex oxides such as (Y–Zr–Ti–O) and (Y–Zr–Ti–Al–O), which is evident from TEM-EDS analysis. Alloy A has a higher hardness (870 VHN) due to the fine grains structure of material compared with alloy B (764 VHN).


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Synthesis and Characterization of 17 Cr Ferritic ODS Steel Developed Through Vacuum Hot Pressing


    Weitere Titelangaben:

    Lect.Notes Mechanical Engineering


    Beteiligte:
    Gascoin, Nicolas (Herausgeber:in) / Balasubramanian, E. (Herausgeber:in) / Dharmalingam, G. (Autor:in) / Prabhukumar, Sellamuthu (Autor:in) / Arun Prasad, M. (Autor:in)


    Erscheinungsdatum :

    2020-09-27


    Format / Umfang :

    10 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Synthesis and Characterization of 17 Cr Ferritic ODS Steel Developed Through Vacuum Hot Pressing

    Dharmalingam, G. / Prabhukumar, Sellamuthu / Prasad, M. Arun | TIBKAT | 2021


    Life prediction of newly developed ferritic stainless steels for automotive muffler

    Chen, Chao / Zheng, Yue / Zhang, Yue et al. | Tema Archiv | 2014


    Evaluation of Ferritic Stainless Steel Performance in Exhaust Environment

    Chauhan, Shiv / Ponkshe, Shripadraj / Polisetti, Venkata Sumanth | SAE Technical Papers | 2022


    New ferritic stainless steel grade for exhaust manifold application

    Robens, Eva / Maillard, Romaric / Gabellone, Davide et al. | Tema Archiv | 2014


    Formability of the ferritic stainless steel for exhaust manifold

    Ozaki, Yoshihiro / Iguchi, Takaaki / Ujiro, Takumi | Tema Archiv | 2008