Abstract Tribological properties of Ti-6Al-4V alloy against GCr15 steel at low temperature in vacuum were measured. The worn surfaces of Ti-6Al-4V alloy specimens were examined by a Hitachi S-570 type scanning electron microscope. The debris were analyzed using a D/max-γB XRD spectrometer. The results showed that the wear rate of Ti-6Al-4V alloy in vacuum ranged within 1.3– 12.0 mg·km–1 at low temperature. The wear rate of Ti-6Al-4V alloy increased with increasing the sliding velocity at low temperature in vacuum. The surface temperature increased to about 32°C for 300 m of sliding distance. It was found that plough characteristics on the worn surface provide information of the adhesion wear. Under the low sliding velocity, microcracks formed on the worn surface indicating damage due to low temperature, while no such microcracks were formed under the higher sliding velocity. The XRD analysis showed that the debris contain Fe, implying that the steel disc was wearing off although the original hardness of the steel was higher than that of the Ti-6Al-4V specimen.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    DRY SLIDING WEAR OF Ti-6Al-4V ALLOY AT LOWTEMPERATURE IN VACUUM


    Beteiligte:
    LIU, YONG (Autor:in) / YANG, DEZHUANG (Autor:in) / HE, SHIYU (Autor:in) / YE, ZHUYU (Autor:in)


    Erscheinungsdatum :

    2006-01-01


    Format / Umfang :

    8 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Oil Circulation Behavior in LowTemperature CO~2 Climate Control Systems

    Hwang, Y. / Cremaschi, L. / Radermacher, R. et al. | British Library Conference Proceedings | 2004



    Dry Sliding Wear of Ti-6Al-4V Alloy at Low Temperature in Vacuum

    Liu, Y. / Yang, D. / He, S. et al. | British Library Conference Proceedings | 2006


    Wear-resistant lifter sliding table

    CHEN JIAYUAN / CHE JINGHUI | Europäisches Patentamt | 2016

    Freier Zugriff

    Sliding Wear Behavior of Chromium Nitride Coated Free Machining Ti-3Al-2V Alloy

    Kim, Y.-S. / Song, J.-H. / Jeong, J.-I. et al. | British Library Conference Proceedings | 1993