Abstract Nano-sized particulate materials have been influencing their effect in the modern world. In this paper, morphological conduct is been decided by using the sandwich sheets of fibre-metal laminates (FMLs) containing nanoclay Cloisite 30B and Mg–Al layered double hydro-oxide (Mg–Al LDH). Atomic force microscope (AFM) is been utilized to discover the harshness of the nano-particles. Here, the tensile test for 3, 4 and 5 wt% of layered double hydroxide (LDH)/nanoclay added FML sheets was analysed. The EDAX is employed to discover the real structure of the chosen nano-powders along the identification of the chemical composition of the nanofiller. It results that the sandwich sheet with nanoclay had smooth surface for a similar molecule measure than the LDH. The fractured surface is analysed by scanning electron microscopy (SEM) hence indicates ductile nature of fracture for modified epoxy and reinforced with glass fibre metal. Henceforth, nanoclay and LDH-based FMLs can be decided on applications in automotive applications.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Experimental Investigation on Tensile and Fracture Behaviour of Glass Fibre-Reinforced Nanoclay/Mg–Al LDH-Based Fibre Metal Laminates


    Beteiligte:


    Erscheinungsdatum :

    2018-12-21


    Format / Umfang :

    11 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Fatigue and fracture of fibre metal laminates

    Alderliesten, René | TIBKAT | 2017


    Fibre metal laminates

    Vlot, A. ;Gunnink, J. W. | British Library Conference Proceedings | 2001


    Impact response of thick glass fibre reinforced polyester laminates

    Zhou,G. / Davies,G.A. / Imperial College,London,GB | Kraftfahrwesen | 1995


    Joints in fibre metal laminates

    BEUMLER THOMAS | Europäisches Patentamt | 2024

    Freier Zugriff