Abstract Since its launch in April 1990, the Hubble Space Telescope (HST) has made many important observations from its vantage point in low Earth orbit (LEO). However, as seen during five servicing missions, the outer layer of multilayer insulation (MLI) has become successively more embrittled and has cracked in many areas. In May 2009, during the 5th servicing mission (called SM4), two MLI blankets were replaced with new insulation pieces and the space-exposed MLI blankets were retrieved for degradation analyses by teams at NASA Glenn Research Center (GRC) and NASA Goddard Space Flight Center (GSFC). The MLI blankets were from Equipment Bay 8, which received direct sunlight, and Equipment Bay 5, which received grazing sunlight. Each blanket contained a range of unique regions based on environmental exposure and/or physical appearance. The retrieved MLI blanket’s aluminized-Teflon® fluorinated ethylene propylene (Al-FEP) outer layers have been analyzed for changes in optical, physical, and mechanical properties, along with space induced chemical and morphological changes. When compared to pristine material, the analyses have shown how the Al-FEP was severely affected by the space environment. This paper reviews tensile properties, solar absorptance, thermal emittance, x-ray photoelectron spectroscopy (XPS) data and atomic oxygen erosion values of the retrieved HST blankets after 19 years of space exposure.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Analyses of Hubble Space Telescope Aluminized-Teflon Insulation Retrieved After 19 Years of Space Exposure


    Beteiligte:


    Ausgabe :

    2013


    Erscheinungsdatum :

    2012-06-04


    Format / Umfang :

    14 pages





    Medientyp :

    Aufsatz/Kapitel (Buch)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Degradation of Hubble Space Telescope aluminized-Teflon bi-stem thermal shields

    Groh, Kim K. de / Snyder, Aaron / Finlay, Katherine A. | Tema Archiv | 2008


    Mechanical properties of teflon FEP retrieved from the Hubble space telescope

    Dever, J.A. / Groh, K.K. de / Messer, R.K. et al. | Tema Archiv | 2001


    Effect of Solar Exposure on the Atomic Oxygen Erosion of Hubble Space Telescope Aluminized-Teflon Thermal Shields

    Guo, Aobo / Ashmead, Claire C. / Groh, Kim K. et al. | Springer Verlag | 2012


    Thermal cycling-caused degradation of Hubble Space Telescope aluminized FEP thermal insulation

    Banks, Bruce / Stueber, Thomas / Rutledge, Sharon et al. | AIAA | 1998


    Surface and bulk degradation of Teflon FEP retrieved from the Hubble Space Telescope solar arrays

    Moser, M. / Semprimoschnig, C.O.A. / Eesbeek, M.R.J. van et al. | Tema Archiv | 2008