In this study, to explore the deterioration mechanism of the surrounding rock-ining by the thermal effect of conflagrations, sandstone-concrete bi-materials with various rough interfaces were produced employing three-dimensional scanning and engraving techniques. Uniaxial compression experiments were performed on bi-materials heat-treated from 25°C to 800°C. Combined with acoustic emission (AE) and digital image correlation (DIC) methods, the coupling effects of interface roughness and treatment temperature on mechanical behavior and fracture characteristics were revealed. The findings show that the mechanical parameters present the “U” change of reducing and then growing with the increase of roughness, which is more noticeable at 25°C and 200°C than 400–800°C. The mechanical parameters continuously reduce with increasing temperature. Internal defects in the specimen increase as the temperature nears 400°C. At 800°C, developed microcracks are discovered in sandstone, concrete, and the intermediate interface. Furthermore, failure modes at 25–200°C and 800°C are predominated by tensile and shear failure, respectively. At 400–600°C, the failure mode shifts progressively from tensile to mixed tensile-shear failure as the roughness increases.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Uniaxial Compressive Behaviors of Sandstone-concrete Binary with Rough Interface after High Temperatures


    Weitere Titelangaben:

    KSCE J Civ Eng


    Beteiligte:
    Su, Haijian (Autor:in) / Wang, Wenbo (Autor:in) / Yu, Liyuan (Autor:in) / Nie, Yinjiang (Autor:in) / Zhang, Luqing (Autor:in) / Liu, Jiawei (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2024-08-01


    Format / Umfang :

    15 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Development and Evaluation for Microdamage of Concrete under Uniaxial Compressive Load

    Wang, Y.T. / Chen, W.Z. / Jiang, F.X. | British Library Conference Proceedings | 2014


    Binary Compressive Tracking

    Jiang Lu, / Ting Zhang, / Qingquan Sun, et al. | IEEE | 2017



    Uniaxial Compression Testing of Sandstone under Microscope: Damage Characteristics and Failure Mechanisms

    Hu, Huarui / Xia, Binwei / Chen, Cancan et al. | Springer Verlag | 2024