Abstract Crack provokes to lose a main performance of watertightness of concrete and leads to accelerate the deterioration of concrete. This brings about reduction of service life of concrete eventually. The background is a good motivation to define a critical crack width to prevent chloride from penetrating through crack in concrete. Since concrete structures have to be proven for a minimum service life, the critical crack width can be regarded as a crucial factor for estimating durability performance and integrity of concrete structures. This study is focused on examining the effect of micro-crack on chloride penetration in concrete and identifying the critical crack width experimentally. Because concrete structures have to meet a minimum service life, crack width must be smaller than the critical crack width. Specimens with different crack width have been subjected to Rapid Chloride Migration testing (RCM). The results of this study show the critical crack width of about 0.013 mm. Cracks smaller than the critical crack width are considered not to have a significant influence on the rate of chloride penetration inwards, while chloride penetration does proceed faster above this critical crack width. Meanwhile, cracked specimens were immersed in artificial seawater for 472 days. The result of this long term experiment indicates critical crack width of 0.04 mm. It is thought that crack healing leads the difference between short and long tem experiment.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Experimental examination on chloride penetration through micro-crack in concrete


    Beteiligte:
    Yoon, In-Seok (Autor:in) / Schlangen, Erik (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2013-12-27


    Format / Umfang :

    11 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Experimental examination on chloride penetration through micro-crack in concrete

    Yoon, In-Seok / Schlangen, Erik | Online Contents | 2014


    Reduced chloride penetration into concrete by means of formwork

    Larsen, C. K. / Stroem, E. O. | British Library Conference Proceedings | 1994


    Effect of Fiber-Reinforced Polymer Wrapping on Concrete Chloride Penetration and Concrete Cover

    Yazdani, Nur / Garcia, Gunther G. | Transportation Research Record | 2014