In this chapter the nucleation and shape development of cracks in longitudinal lap joints under static and fatigue loading will be considered. The issues of special attention are the influence of a squeeze force on the mode of fatigue failure and the significance of fretting on a sheet interface for fatigue crack initiation.
Crack Initiation Location and Crack Shape Development in Riveted Lap Joints – Experimental Trends
Solid Mechanics, Applicat.
2012-05-17
22 pages
Aufsatz/Kapitel (Buch)
Elektronische Ressource
Englisch
Fatigue Crack Growth in Riveted Joints
British Library Conference Proceedings | 1997
|Multiple Crack Initiation and Crack Growth Riveted Lap Joint Specimens
British Library Conference Proceedings | 1995
|Fatigue Crack Growth Predictions in Riveted Joints
British Library Conference Proceedings | 1999
|Fatigue crack location and fatigue life for riveted lap joints in aircraft fuselage
Tema Archiv | 2014
|Fretting Crack Nucleation in Riveted Lap Joints - Predictions and Experiments
British Library Conference Proceedings | 1999
|